- Effect of Crystallization Treatment on the Magnetic Properties of Amorphous Strips Based on Co-Fe-Ni-B-Si-Cr Containing Nitrogen
-
H.J. Cho, H.T. Kwon, H.H. Ryu, K.Y. Sohn, B.S. You, W.W. Park
-
J Korean Powder Metall Inst. 2006;13(4):285-289.
-
DOI: https://doi.org/10.4150/KPMI.2006.13.4.285
-
-
 Abstract
 PDF
- Co-Fe-Ni-B-Si-Cr based amorphous strips containing nitrogen were manufactured via melt spinning, and then devitrified by crystallization treatment at the various annealing temperatures of 300°Csim540°C for up to 30 minutes in an inert gas (N_2) atmosphere. The microstructures were examined by using XRD and TEM and the magnetic properties were measured by using VSM and B-H meter. Among the alloys, the amorphous ribbons of Co_72.6Fe_9.8Ni_5.5B_2.4Si_7.1Cr_2.6 containing 121 ppm of nitrogen showed relatively high saturation magnetization. The alloy ribbons crystallized at 540°C showed that the grain size of Co_72.6Fe_9.8Ni_5.5B_2.4Si_7.1Cr_2.6 alloy containing 121 ppm of nitrogen was about f nm, which exhibited paramagnetic behavior. The formation of nano-grain structure was attributed to the finely dispersed Fe4N particles and the solid-solutionized nitrogen atoms in the matrix. Accordingly, it can be concluded that the nano-grain structure of 5nm in size could reduce the core loss within the normally applied magnetic field of 300A/m at 10kHz.
|
kpmi